dc.contributor.authorDienstmann, Fernando Konarzewskipt_BR
dc.contributor.authorFühr, Luciane Taispt_BR
dc.contributor.authorScheffel, Leonardo Felixpt_BR
dc.contributor.authorCarone, Carlos Leonardo Pandolfopt_BR
dc.contributor.authorMorisso, Fernando Dal Pontpt_BR
dc.contributor.authorSchneider, Eduardo Luíspt_BR
dc.contributor.authorKunst, Sandra Raquelpt_BR
dc.contributor.authorFerreira, Jane Zoppaspt_BR
dc.contributor.authorOliveira, Cláudia Trindadept_BR
dc.date.accessioned2021-07-07T04:34:17Zpt_BR
dc.date.issued2021pt_BR
dc.identifier.issn2176-1515pt_BR
dc.identifier.urihttp://hdl.handle.net/10183/223335pt_BR
dc.description.abstractO Zamac tem sido utilizado na indústria galvânica, principalmente, devido ao seu baixo ponto de fusão, o que permite a obtenção de peças com riqueza de detalhes, tais como peças do setor moveleiro, moda e metais sanitários. No entanto, os processos de sua obtenção, por injeção sob pressão e injeção centrífuga, geram porosidade e, consequentemente, aumento de sucata. Por outro lado, estudos mostraram que fusão por gravidade não apresenta tais problemas. Nesse sentido, o objetivo deste artigo foi tratar termicamente peças de Zamac injetadas sob pressão, com a finalidade de obter comportamento semelhante às peças fundidas por gravidade. Para tanto, peças injetadas sob pressão foram tratadas termicamente, abaixo da temperatura de fusão. A caracterização morfológica dessas amostras foi obtida por MEV. Observou-se que o tratamento térmico acima da temperatura eutetoide apresentou melhor resultado com respeito à porosidade observada.pt_BR
dc.description.abstractThe Zamac has been used in the galvanic industry mainly due its low fusing point properties, which allows obtaining very detailed parts, like parts for furniture industry, fashion and health metals. However, its production processes, like pressure injection and centrifugal injection, generate an increase in porosity as well as waste. On the other hand, studies show that die casting leaked Zamac doesn’t show the same problems. In this sense, the goal for this work is to perform heat treatment in Zamac parts produced by pressure injection in order to obtain similar properties as the ones produced by die casting leakage. For this, the parts injected under pressure were thermally treated under their fusion temperature. It was observed that thermic treatment over the eutectoid temperature showed the best result, regarding the observed porosity.en
dc.format.mimetypeapplication/pdfpt_BR
dc.language.isoengpt_BR
dc.relation.ispartofTecnologia em metalurgia, materiais e mineração. São Paulo, SP. Vol. 18 (2021), Art. e2070, 8 p.pt_BR
dc.rightsOpen Accessen
dc.subjectZamacen
dc.subjectLigas metálicaspt_BR
dc.subjectTratamento térmicopt_BR
dc.subjectPorosityen
dc.subjectPorosidadept_BR
dc.subjectHeat treatmenten
dc.titleTratamento térmico em Zamac visando diminuir defeitos de porosidadept_BR
dc.typeArtigo de periódicopt_BR
dc.identifier.nrb001127627pt_BR
dc.type.originNacionalpt_BR