Titanate nanotubes produced from microwave-assisted hydrothermal synthesis : characterization, adsorption and photocatalytic activity
Visualizar/abrir
Data
2017Tipo
Assunto
Abstract
A microwave-assisted hydrothermal (MAH) method was employed to synthesize TiO2 nanotubes (TNTs) and these were compared to the conventional hydrothermal (CH) method. The nanotubes were characterized for their crystallinity, morphology, surface area and photocatalytic activity. The TiO2 P25 was used for comparison purposes and efficiently degraded both dyes. However, methylene blue was adsorbed on the nanotube surfaces, which can be attributed to the electrostatic interaction between the cationi ...
A microwave-assisted hydrothermal (MAH) method was employed to synthesize TiO2 nanotubes (TNTs) and these were compared to the conventional hydrothermal (CH) method. The nanotubes were characterized for their crystallinity, morphology, surface area and photocatalytic activity. The TiO2 P25 was used for comparison purposes and efficiently degraded both dyes. However, methylene blue was adsorbed on the nanotube surfaces, which can be attributed to the electrostatic interaction between the cationic methylene blue and the negatively charged TNT surface. On the other hand, all nanotubes had a photocatalytic performance with methyl orange (anionic dye). Additional degradation was observed for nanotubes synthesized via the MAH method at 150 °C. This can be directly related to their larger surface area. Adsorption mechanisms of TNTs were also discussed by applying the Langmuir and Freundlich isotherm. The results show an efficient dye wastewater treatment through the application of TNT photocatalyst. ...
Contido em
Brazilian journal of chemical engineering. São Paulo, SP. Vol. 34, no. 1 (Jan./Mar. 2017), p. 331-339
Origem
Nacional
Coleções
-
Artigos de Periódicos (39580)Engenharias (2413)
Este item está licenciado na Creative Commons License