UHMWPE-layered silicate nanocomposites by in situ polymerization with tris(pyrazolyl)borate titanium/clay catalyst
![Thumbnail](/bitstream/handle/10183/24593/000705593.pdf.jpg?sequence=3&isAllowed=y)
Visualizar/abrir
Data
2009Autor
Tipo
Assunto
Resumo
Nanocompósitos de polietileno-MMT foram preparados através da metodologia de polimerização in situ utilizando TpMs*TiCl3 (1) intercalado na galeria da Cloisite 30B (C30B) e na presença de metilaluminoxano (MAO) como ativador. Através da análise de difração de raios-X (DRX) foi observado que o espaçamento basal da argila ativada muda de 1,85 nm (2θ = 4,8) para 2,18 nm (2θ = 4,0) indicando a ocorrência da intercalação do catalisador de titânio na galeria da argila. O sistema catalítico 1/C30B/MA ...
Nanocompósitos de polietileno-MMT foram preparados através da metodologia de polimerização in situ utilizando TpMs*TiCl3 (1) intercalado na galeria da Cloisite 30B (C30B) e na presença de metilaluminoxano (MAO) como ativador. Através da análise de difração de raios-X (DRX) foi observado que o espaçamento basal da argila ativada muda de 1,85 nm (2θ = 4,8) para 2,18 nm (2θ = 4,0) indicando a ocorrência da intercalação do catalisador de titânio na galeria da argila. O sistema catalítico 1/C30B/MAO foi ativo na polimerização do etileno sob diferentes condições reacionais. A morfologia esfoliada do nanocompósito PE-MMT foi confirmada pela análise de difração de raios-X (DRX) e microscopia eletrônica de transmissão (MET). A presença de argila esfoliada (5% em peso) na matriz polimérica confere melhores propriedades mecânicas (módulo de flexão e módulo de armazenamento) quando comparada com aquelas apresentadas pelo polietileno puro produzido exclusivamente por 1. ...
Abstract
Polyethylene-MMT nanocomposites were prepared by in situ polymerization methodology using TpMs*TiCl3 (1) intercalated into the gallery of Cloisite 30B (C30B) using methylaluminoxane (MAO) as activator. From the powder X-ray diffraction (XRD) analysis it was observed that the basal spacing of the activated organoclay changes from 1.85 nm (2θ = 4.8) to 2.18 nm (2θ = 4.0) indicating that the intercalation of the titanium catalyst into the gallery took place. The catalytic system 1/C30B/MAO was ac ...
Polyethylene-MMT nanocomposites were prepared by in situ polymerization methodology using TpMs*TiCl3 (1) intercalated into the gallery of Cloisite 30B (C30B) using methylaluminoxane (MAO) as activator. From the powder X-ray diffraction (XRD) analysis it was observed that the basal spacing of the activated organoclay changes from 1.85 nm (2θ = 4.8) to 2.18 nm (2θ = 4.0) indicating that the intercalation of the titanium catalyst into the gallery took place. The catalytic system 1/C30B/MAO was active in the ethylene polymerization under different reaction conditions. The exfoliated morphology of the PE-MMT nanocomposite was further examined and confirmed by X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis. The presence of exfoliated clay (5 wt.%) in the PE matrix confers better mechanical properties (flexural modulus and storage modulus) when compared with the ones displayed by the neat PE produced using exclusively 1. ...
Contido em
Journal of the Brazilian Chemical Society. São Paulo. Vol. 20, n. 3 (2009), p. 472-477